图片名称
img

NEWS CENTER

NEWS CENTER

0757-86688585
rds
He first layer was a cubic TiC, and the second layer was a slender or cylindrical TiC.

He first layer was a cubic TiC, and the second layer was a slender or cylindrical TiC.

Pakistan's FAKhalid et al. used the method of brazing in a vacuum furnace to study the microstructure of the diamond interface with Cu-14.4Sn-10.2Ti-1.5Zr alloy as the brazing filler metal. Brazing process: vacuum degree 2×10-8Pa, brazing temperature 930°C, holding time 10min, cooling rate 20°C/min.

25

2023

/

05

The electric steelmaking control model is divided into a static model and a dynamic model.

The electric steelmaking control model is divided into a static model and a dynamic model.

The connotation of electric furnace automatic steelmaking can be divided into two levels: the first level, instead of entering (hand) for oxygen blowing, power supply and feeding operations, and the automatic determination of the smelting end point, this level is still called automatic steelmaking;

25

2023

/

05

The above studies show that different solder alloys

The above studies show that different solder alloys

Pakistan's FAKhalid et al. used the method of brazing in a vacuum furnace to study the microstructure of the diamond interface with Cu-14.4Sn-10.2Ti-1.5Zr alloy as the brazing filler metal. Brazing process: vacuum degree 2×10-8Pa, brazing temperature 930°C, holding time 10min, cooling rate 20°C/min.

25

2023

/

05

Electric furnace automatic steelmaking production control model

Electric furnace automatic steelmaking production control model

The connotation of electric furnace automatic steelmaking can be divided into two levels: the first level, instead of entering (hand) for oxygen blowing, power supply and feeding operations, and the automatic determination of the smelting end point, this level is still called automatic steelmaking;

07

2018

/

12

Process and method for brazing diamond by copper base alloy brazing material

Process and method for brazing diamond by copper base alloy brazing material

Pakistan's FAKhalid et al. used the method of brazing in a vacuum furnace to study the microstructure of the diamond interface with Cu-14.4Sn-10.2Ti-1.5Zr alloy as the brazing filler metal. Brazing process: vacuum degree 2×10-8Pa, brazing temperature 930°C, holding time 10min, cooling rate 20°C/min.

07

2018

/

12

< 1 >
rds

Foshan Rongdongsheng Furnace Co., Ltd.

TEL：0757-86688585

Company Address: North End of Hongxing Road, Shishan, Nanhai District, Foshan City, Guangdong Province

TEL：0757-86688585

FAX：0757-86688590

TEL：Mr Qin 13074282589

erweima
erweima
京ICP备10002622号-38
Copyright © 2023 Foshan Rongdongsheng Furnace Co., Ltd. Powered By: 300.cn SEO Business license